Peter Paul has developed a proprietary epoxy molding system. The system is designed to run very fast molding cycles with excellent shelf stability. Also, this system requires low transfer pressures for optimum fill properties. The material is mineral filled and fiber re-enforced and will meet a UL 94 V-O flammability. Being of this system exhibits excellent moisture protection and lead adhesion.
Vpoxy a revolutionary epoxy molding system designed to run very fast molding cycles with excellent shelf stability. Also, this system requires low transfer pressures for optimum fill properties. The material is mineral filled and fiber re-enforced and will meet a UL 94 flammability. Being of this system exhibits excellent moisture protection and lead adhesion.
Vpoxy is a soft flow mineral filled fiberglass reinforced epoxy molding compound. This material was designed to be molded in both transfer and screw injection molding equipment. Vpoxy exhibits exceptional shelf stability while still being rapid cure. Additionally, Vpoxy is considerably less abrasive than ordinary silica filled materials.
|Bulk Density gm/cc||.90|
|Spiral Flow (in)||30 – 40|
|Hot Plate Cure (sec)||30 – 40|
|Molded Density gm/cc||2.00|
|Mold Shrinkage cc/cm||0.006|
|Glass Transition Temperature (Tg)||110°C|
cal/cm-sec-°C x 10⁴
|Max Intermittent Operation Temperature||°C 210|
|Flexural Strength kg/cm2||1,100|
|Tensile Strength kg/cm2||750|
|Hardness, Shore D||90|
|Izod Impact kg-m/cm of notch||0.022|
|Dielectric Constant, 1 KHz||4.7|
|Dissipation Factor, 1 KHz||0.006|
|Loss Factor 1 KHz||0.020|
|Arc Resistance, seconds||190|
|Dielectric Strength v/mil||450|
*Values based on generic testing for this type system. Subject to revision.
Storage & Handling
Material should be stored in closed and sealed containers. Allow refrigerated material to equilibrate to room temperature before opening.
|Shelf Life *
@ 72º F
* Defined as a loss of flow not to exceed 40% of original.